類別: PMMA VR-S40
功能:高耐沖擊材料
生產(chǎn)廠商:三菱麗陽(yáng)株式會(huì)社
原料技術(shù)數(shù)據(jù)
性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
基本性能 |
吸水率 |
24hr |
ASTM D-570 |
0.4 |
% |
熔體流動(dòng)速率 |
230°C 3.8kg |
ASTM D-1238 |
7.8 |
g/10min |
物理性能 |
成形收縮率 |
--- |
ASTM D-955 |
0.3-0.7 |
% |
折射率 |
--- |
ASTM D-542 |
1.49 |
nd |
比重 |
--- |
ASTM D-792 |
1.16 |
--- |
全光線透射系數(shù) |
3.2mm |
ASTM D-1003 |
92 |
% |
機(jī)械性能 |
抗拉強(qiáng)度 |
ASTM NO.* |
ASTM D-638 |
440 |
Kg/cm2 |
延展率 |
ASTM NO.* |
ASTM D-638 |
90 |
% |
抗彎強(qiáng)度 |
1/4"棒 |
ASTM D-790 |
615 |
Kg/cm2 |
彎曲彈性模量 |
1/4"棒 |
ASTM D-790 |
2.0×104 |
Kg/cm2 |
懸臂梁式?jīng)_擊強(qiáng)度 |
1/4"付 |
ASTM D-256 |
11 |
kg.cm/cm |
洛氏硬度 |
M scale |
ASTM D-785 |
59 |
--- |
電氣性能 |
表面電阻系數(shù) |
--- |
JIS K-6911 |
>1×1016 |
Ω |
體積電阻系數(shù) |
--- |
JIS K-6911 |
>1×1015 |
Ω.m |
絕緣擊穿強(qiáng)度 |
--- |
JIS K-6911 |
15 |
kv/mm |
介電常數(shù) |
--- |
JIS K-6911 |
3.9 |
60HZ |
介質(zhì)損耗角正切 |
60HZ |
JIS K-6911 |
0.04 |
--- |
耐電弧性 |
--- |
JIS K-6911 |
沒(méi)有痕跡 |
--- |
熱 性 能 |
維卡軟化點(diǎn) |
1kg |
ASTM D-1525 |
97 |
°C |
比熱 |
--- |
--- |
0.35 |
cal/g/°C |
線膨脹系數(shù) |
--- |
ASTM D-696 |
9.5×10-5 |
cm/cm/°C |
熱傳導(dǎo)系數(shù) |
--- |
ASTM C-177 |
5×10-4 |
cal/s/cm/°C |
載荷撓曲溫度 |
18.56kg/cm2 |
ASTM D-648 |
82 |
°C |